The influence of SO2(g) on the atmospheric corrosion of Mg-Al alloys
https://www.sintef.no/publikasjoner/publikasjon/?pubid=1338625
Daniel Blucher
.
Daniel Blucher
.
Telefon:
930 06 103
E-post:
Enhet:
SINTEF Industri
Avdeling:
Materialer og nanoteknologi
Kontorsted:
Trondheim
Publikasjoner og ansvarsområder
Publikasjon
A New Cast Ni-Base Alloy Suitable for Severe Sour Service
https://www.sintef.no/publikasjoner/publikasjon/?pubid=1345727
Publikasjon
A new cast Ni-base alloy suitable for severe sour service
https://www.sintef.no/publikasjoner/publikasjon/?pubid=1401731
This paper reports the recent findings on corrosion resistance of a new centrifugally cast austenitic corrosion resistant alloy (CRA), 46Ni-35Cr-9Mo, against severe sour gas environment. The sour service corrosion validation was carried out by sulphide stress cracking (SSC) using autoclaves with fou...
Publikasjon
A new centrifugally cast austenitic Ni-base alloy suitable for severe sour service heavy wall thickness piping application
https://www.sintef.no/publikasjoner/publikasjon/?pubid=1421868
Publikasjon
Characterization of different corrosion protection systems on magnesium alloys for applications in the automotive industry
https://www.sintef.no/publikasjoner/publikasjon/?pubid=1421858
Publikasjon
New insights into the corrosion of magnesium alloys — The role of aluminum
https://www.sintef.no/publikasjoner/publikasjon/?pubid=1322725
The atmospheric corrosion of several Mg–Al alloys was investigated at − 4, 4 and 22 °C. The rate of corrosion increased with increasing temperature and decreasing Al content. Also, the effect of temperature became stronger with increasing Al content. The cast microstructure was found to influence bo...
Publikasjon
Corrosion in water filled galvanized pipes
https://www.sintef.no/publikasjoner/publikasjon/?pubid=1249151
Publikasjon
Atmospheric corrosion of Mg alloy AZ91D fabricated by a semi-solid casting technique: The influence of microstructure
https://www.sintef.no/publikasjoner/publikasjon/?pubid=1249114
The atmospheric corrosion behavior of alloy AZ91D produced by a semi-solid metal (SSM) technique and by conventional high pressure die casting (HPDC) was investigated for up to 1176 hours in the laboratory. Alloy AZ91D in the SSM state was fabricated using a rheocasting (RC) technique in which the s...
Publikasjon
Der Einfluss von SO2 auf die atmosphärische Korrosion von Mg- und Mg-Al-Legierungen
https://www.sintef.no/publikasjoner/publikasjon/?pubid=1249148
Publikasjon
Atmosperic corrosion analysis of the dissimilar friction stir welded joint of AM50 Mg alloy to 6005-T6 Al alloy
https://www.sintef.no/publikasjoner/publikasjon/?pubid=1265861