The suspension cables of the Lysefjord Bridge in Norway are an example of long term development of wire fractures. During the sixteen years of operation about 1600 wire fractures have been registered in the outer layer of the Z-wire. The accumulation of wire fractures follows so far a quite linear d...

Forfattere Lange Hans Iver
År 2013
Type Konferansebidrag og faglig presentasjon
Publikasjon
https://www.sintef.no/publikasjoner/publikasjon/?pubid=CRIStin+1269275

Burst tests of line pipes containing high-pressure hydrogen and methane gas were conducted (i.e. Test 3 and Test 4). The pipes tested were X65 ERW pipes with 267mm outer diameter and 6mm wall thickness. Applied internal pressure was 15MPa. A 300mm long crack was initiated by a shaped charge.  Unstab...

Forfattere Lange Hans Iver
År 2008
Type Rapport/avhandling
Publikasjon
https://www.sintef.no/publikasjoner/publikasjon/?pubid=CRIStin+1269273

Burst tests of line pipes containing high-pressure hydrogen and methane gas were conducted (i.e. Test 3 and Test 4). The pipes tested were X65 ERW pipes with 267mm outer diameter and 6mm wall thickness. Applied internal pressure was 15MPa. A 300mm long crack was initiated by a shaped charge.  Unstab...

Forfattere Lange Hans Iver
År 2008
Type Rapport/avhandling
Publikasjon
https://www.sintef.no/publikasjoner/publikasjon/?pubid=CRIStin+1269271

...  Burst tests of line pipes containing high-pressure hydrogen and methane gas were conducted. The pipes tested were X65 ERW pipes with 267mm outer diameter and 6mm wall thickness. Applied pressures were 12MPa. A 300mm long crack was initiated by a shaped charge.  Unstable shear fracture propagated a...

Forfattere Lange Hans Iver
År 2008
Type Rapport/avhandling