Effect of thermal residual stresses on ductile-to-brittle transition of a bi-material specimen by using the CAFE method

Effect of thermal residual stresses on ductile-to-brittle transition of a bi-material specimen by using the CAFE method

Kategori
Tidsskriftspublikasjon
Sammendrag
The effect of residual stress on fracture of materials or structures has been widely studied. However, its influence on ductile-to-brittle transition (DBT), a crucial phenomenon of structural materials, has rarely been investigated so far. In the present study, employing the eigenstrain method residual stresses are introduced into a bi-material specimen, where two configurations of crack and interface, e.g., one with interface perpendicular and one parallel to the crack extension, are designed to study the influence of residual stress. The DBT of the bi-material specimen in the presence of residual stresses is numerically studied by using the CAFE method where temperature dependent surface energy is implemented to calculate absorbed energy of Charpy impact testing specimen. It is found that residual stress generated in the two configurations affect the DBT in a similar manner. The DBT curves generally shift to higher temperature due to the decrease of absorbed energy with the increase of residual stress. It is found that the decrease of absorbed energy in both configurations is caused by the additional constraint on the notch root, which is induced by the residual stress and can facilitate the fracture.
Oppdragsgiver
  • Norges forskningsråd / 228513
Språk
Engelsk
Forfatter(e)
Institusjon(er)
  • Norges teknisk-naturvitenskapelige universitet
  • SINTEF Industri / Materialer og nanoteknologi
År
2020
Publisert i
European Journal of Mechanics. A, Solids
ISSN
0997-7538
Årgang
80
Side(r)
1 - 12