Surface stability of epitaxial La0.7Sr0.3MnO3 thin films on (111)-oriented SrTiO3

Surface stability of epitaxial La0.7Sr0.3MnO3 thin films on (111)-oriented SrTiO3

Kategori
Vitenskapelig artikkel
Sammendrag
We report on the stability of the La0.7Sr0.3MnO3 thin film surface when deposited on (111)-oriented SrTiO3. For ultrathin La0.7Sr0.3MnO3 films, an initial 3-dimensional morphology is observed, which becomes 2-dimensional with increasing film thickness. For even thicker samples, we show that the surface morphology evolves from 2-dimensional to 3-dimensional and that this observation is consistent with an Asaro-Tiller-Grinfeld instability, which can be controlled by the deposition temperature. This allows for synthesis of films with step-and-terrace surfaces over a wide range of thicknesses. Structural characterization by x-ray diffraction and transmission electron microscopy shows that the films are strained to the SrTiO3 substrate and reveals the presence of an elongated out-of-plane lattice parameter at the interface with SrTiO3.
Språk
Engelsk
Forfatter(e)
  • Ingrid Hallsteinsen
  • Jos Emiel Boschker
  • Magnus Kristofer Nord
  • S Lee
  • M Rzchowski
  • Per Erik Vullum
  • Jostein Grepstad
  • Randi Holmestad
  • CB Eom
  • Thomas Tybell
Institusjon(er)
  • Norges teknisk-naturvitenskapelige universitet
  • University of Wisconsin-Madison
  • SINTEF Industri / Materialer og nanoteknologi
År
Publisert i
Journal of Applied Physics
ISSN
0021-8979
Forlag
American Institute of Physics (AIP)
Årgang
113
Hefte nr.
18