Introduction The only viable solution to reduce 20% of the greenhouse gas emissions is to develop and implement carbon dioxide (CO2) capture and sequestration technologies. Despite the development of new polymeric materials for CO2 capture membranes such as thermal rearranged polymers (TR...

Forfattere Marius Sandru Eugenia Mariana Sandru Per Martin Stenstad Taek-Joong Kim Jing Deng Liyuan Deng
År 2018
Type Poster
Publikasjon
https://www.sintef.no/publikasjoner/publikasjon/1599308/

Despite the development of many new polymeric materials for CO2 capture membranes, only few membranes have arrived to testing at pilot scale. This clearly indicates the need of new strategies for membrane fabrication. One of membrane preparation approaches employed in the POLYMEM project is based...

Forfattere Marius Sandru Eugenia Sandru Per Martin Stenstad Taek-Joong Kim Jing Deng Liyuan Deng
År 2017
Type Poster
Publikasjon
https://www.sintef.no/publikasjoner/publikasjon/1166325/

The hybrid fixed-site-carrier (FSC) membranes were prepared by coating the carbon nanotubes (CNTs) reinforced polyvinylamine (PVAm)/polyvinylalcohol (PVA) blend selective layer on the top of the polysulfone (PSf) ultrafiltration membranes. The influences of membrane preparation parameters of support...

Forfattere Xuezhong He Taek-Joong Kim May-Britt Hagg
År 2014
Type Vitenskapelig artikkel
Publikasjon
https://www.sintef.no/publikasjoner/publikasjon/1022511/

Polyvinyamine (PVAm) Fixed-Site-Carrier (FSC) composite membrane has been reported to have a good potential to be applied for large scale for CO2 capture applications with respect to high permeance and high selectivity. In this study, the membrane was investigated with respect to pH of the casting...

Forfattere Taek-Joong Kim Helene Konstansia Vrålstad Marius Sandru May-Britt Hagg
År 2013
Type Vitenskapelig artikkel