Synthesis and characterization of hybrid aminopropyl silane-based coatings on stainless steel substrates

Synthesis and characterization of hybrid aminopropyl silane-based coatings on stainless steel substrates

Kategori
Tidsskriftspublikasjon
Sammendrag
Transparent and homogeneous hybrid aminopropyl silane-based coatings on steel were prepared by the sol–gel method using hydrolyzed γ-APS as a precursor. The coatings were fabricated by dip coating, and the effect of pH, water/silane ratio and solvent/silane ratio during the coating process was investigated with respect to thermal stability, coating thickness, roughness, contact angle and abrasion resistance. The thickness of the coatings was controlled by the preparation conditions as well as the viscosity of the sols and varied between 0.17 and 4.1 μm. The coatings were in general smooth and the roughness was in the order of a few nanometer. The coatings possessed hydrophilic character with contact angles of water from 65 to 80°, while organic pentadecane wetted the coatings. The abrasion resistance improved with decreasing pH of the water used during hydrolysis of the silane. The abrasion resistant properties of the coatings were characterized with respect to delamination and smearing. Thicker coatings were delaminated while thinner coatings were smeared and displayed lubricating properties. The coatings were thermally stable up to 350 °C, and also displayed a low pore volume and a low surface area.
Oppdragsgiver
  • Norges forskningsråd / 180038
Språk
Engelsk
Forfatter(e)
  • Hanetho Sidsel Meli
  • Kaus Ingeborg
  • Simon Christian
  • Bouzga Aud Mjærum
  • Grande Tor
  • Einarsrud Mari-Ann
Institusjon(er)
  • Norges teknisk-naturvitenskapelige universitet
  • SINTEF Industri / Bærekraftig energiteknologi
  • SINTEF Industri / Materialer og nanoteknologi
  • SINTEF Industri / Prosessteknologi
År
2014
Publisert i
Surface & Coatings Technology
ISSN
0257-8972
Årgang
238
Side(r)
1 - 8