Experimental measurement of temperature-dependent equivalent stress-strain curves of a 420 MPa structural steel with axisymmetric notched tensile specimens

Experimental measurement of temperature-dependent equivalent stress-strain curves of a 420 MPa structural steel with axisymmetric notched tensile specimens

Kategori
Vitenskapelig artikkel
Sammendrag
Recently, the authors in this paper proposed a correction function to determine material’s equivalent stress-strain curve with axisymmetric-notched tensile specimens. In this study, tensile tests were performed at room temperature, -30℃ and -60℃ with axisymmetric notched tensile specimens to verify this method and to identify the equivalent stress-strain curves of a 420 MPa structural steel. A high-speed camera was used together with the so-called edge-tracing method to calculate average true strain. The material’s equivalent stress-strain curve was also measured with extensometer and smooth round bar specimens. Experimental results show that equivalent stress-strain curve of this structural steel is sensitive to test temperature. Equivalent stress-stress curves obtained from axisymmetric notched tensile specimens by using the proposed correction function show good agreement with those from extensometer before diffuse necking and from Bridgman correction at large strain using smooth tensile specimens. Since fracture strain strongly depends on the notch geometry, it is recommended to use axisymmetric notched tensile specimens with smaller when applying the proposed correction function to measure material’s equivalent stress-strain curve.
Oppdragsgiver
  • Research Council of Norway (RCN) / 228513
Språk
Engelsk
Forfatter(e)
  • Shengwen Tu
  • Xiaobo Ren
  • Jianying He
  • Zhiliang Zhang
Institusjon(er)
  • Norges teknisk-naturvitenskapelige universitet
  • SINTEF Industri / Materialer og nanoteknologi
År
2019
Publisert i
Engineering Failure Analysis
ISSN
1350-6307
Årgang
100
Side(r)
312 - 321