Sammendrag
The effects of 3%–50% pre-deformation following solution heat treatment on the age hardening of an Al-3Mg-1Cu alloy have been investigated by Vickers microhardness measurement, tensile tests, differential scanning calorimetry, scanning electron microscopy, and transmission electron microscopy. Pre-deformation has a strong effect on subsequent age-hardening behavior. The precipitation was accelerated, hardness peaks appeared earlier, formation of clusters was inhibited, and a larger fraction of precipitates was observed along the dislocation lines. The contribution of the precipitates to the hardness was evaluated by dissolution tests. It was found that pre-deformation followed by artificial aging resulted in a good strength-elongation balance. The results are significant for the development of combined mechanical deformation and heat treatment processes.