Effect of Elastic Modulus on the Tangential AC Breakdown Strength of Polymer Interfaces

Abstract

Solid-solid interfaces between insulating materials dictate the long-term electrical properties of the complete insulation system. This paper presents theoretical and experimental investigations aiming to address the impact of the material elasticity on tangential AC breakdown strength (BDS) of interfaces between polymers. Four different polymers with different elastic moduli were tested using: Cross-linked polyethylene (XLPE), filled epoxy resin (EPOXY), polyether ether ketone (PEEK) and silicone rubber (SiR). The interfaces were formed between identical specimens and were breakdown tested at various contact pressures. It was found that elastic modulus and contact pressure had pronounced effects on the BDS of interfaces. Higher elastic modulus correlated with decreased BDS by a factor of 1.6 at the same contact pressure. On the other hand, the increase of contact pressure by a factor of 3 elevated the interfacial BDS by a factor of 1.4 in the case of the lowest elastic modulus (SiR-SiR) whereas that for the highest modulus (PEEK-PEEK) was about 2.4 times higher. Using the proposed theoretical approach, we postulated that discharged cavities govern the interfacial BDS at the interface together with the electric treeing resistance of contact area between the cavities. Although the electrical treeing resistance increases with a higher modulus, local field enhancements due to discharged cavities also increase significantly. Therefore, the observed reduction of the BDS with the increase of the elastic modulus is ascribed to the larger cavity size and hence the smaller contact area. It is concluded that increased elastic modulus reduces the dominance of the discharged cavities over the interface breakdown and increase the governance of the electrical treeing resistance of the contact spots.
Read the publication

Category

Academic article

Language

English

Author(s)

Affiliation

  • SINTEF Energy Research / Elkraftteknologi
  • Norwegian University of Science and Technology

Year

2019

Published in

IEEE transactions on dielectrics and electrical insulation

ISSN

1070-9878

Volume

26

Issue

1

Page(s)

211 - 219

View this publication at Norwegian Research Information Repository