Compression stress relaxation in carbon black reinforced HNBR at low temperatures

Abstract

Findings of a study of stress relaxation behaviour of hydrogenated nitrile butadiene rubber (HNBR) at nominal compressive strains up to 0.4 and temperatures above and below the glass transition temperature Tg are reported. Two formulations of a model HNBR with 36% acrylonitrile content and carbon black (CB) loading of 0 and 50 phr were investigated. The relaxation function of HNBR is found to be independent of strain at temperatures right above the Tg or at times longer than 10−3 s for the deformations employed. CB imparts higher long-term stiffness and also larger relaxation strength at times longer than 10−4 s to the HNBR, but it does not affect the relaxation behaviour of the rubber in the time span from 10−3 – 104 s. In addition, the relationship between the strain energy function of HNBR and temperature is demonstrated to have a complex concave-downward shape which is affected by two competing contributions of entropy elasticity and the stress relaxation.
Read the publication

Category

Academic article

Language

English

Author(s)

Affiliation

  • SINTEF Industry / Materials and Nanotechnology
  • Norwegian University of Science and Technology

Year

2017

Published in

Polymer testing

ISSN

0142-9418

Volume

63

Page(s)

226 - 235

View this publication at Norwegian Research Information Repository