Two 6xxx alloys with different Mn-content have been homogenised in a furnace at 575 oC for 2 hours and 15 minutes. Three different heating rates to the homogenisation holding temperature were chosen, as this was expected to affect the precipitation behaviour of the dispersoids. The study focused on developing a reliable procedure for the characterization of the density and spatial distribution of dispersoids in aluminium alloys; both in terms of sample preparation, microscopic techniques and quantitative analyses of results. Scanning electron microscopy (SEM) has been used to evaluate the dispersoid characteristics for the different alloys and heating rates. The results indicate an increase in dispersoid number density and a more uniform distribution of dispersoids for the lowest heating rate, as compared to the more rapid heating rates, for the alloy with 0.05 wt% Mn. For the alloy with 0.15 wt% Mn the number density increased with the heating rate. This is suggested to be due to particle coarsening as an effect of the low heating rate where the samples spend longer time in the furnace.